| FX 998N | ||||||||||||||||||||||
| Классификация |
| Flux 995N | EN 760 : | A AB1 67 AC H51 | ||||||||||||||||||||
| флюс / проволока | AWS A5.23 | EN756 TR | ||||||||||||||||||||
| FX 998N / L 70 | S 4T 2 AB S2Mo | |||||||||||||||||||||
| FX 998N / LNS140TB | F9A2-EG-G | S 5T 5 AB S0 | ||||||||||||||||||||
| Назанчение |
| FX998N is a neutral, agglomered flux intended for the double submerged arc welding (DSW) oflongitudinal seam pipe with a wall thickness greater than 7mm. It can be used with up to 5arcs. When welded in conjunction with LNS 140TB wire, it provides excellent CVN impacttoughness even at very low temperature (-60°C) |
| Одобрение международных агенств |
|
BV |
CRS |
CTL |
DB |
DNV |
PRS |
GL |
LR |
RINA |
RMRS |
TüV |
UDT |
|||||||||
|
LNS165 / FX998N |
|
+ |
|
|
|
|
|
|
|
|
|
+ |
||||||||
| Химический состав наплавленного металла в комбинации, % |
| проволока |
C |
Mn |
Si |
P |
S |
Ni |
Mo |
|
|
| LNS160 |
0.07 |
1.00 |
0.10 |
0.02 |
0.015 |
1.00 |
|||
| LNS162 |
0.08 |
1.00 |
0.10 |
0.02 |
0.015 |
2.00 |
|
|
|
| LNS165 |
0.07 |
1.30 |
0.20 |
0.02 |
0.015 |
0.90 |
0.20 |
||
| Механические свойства наплавленного металла в комбинации |
|
|
предел текучести |
предел прочности |
удар ISO-V ( J ) |
||
|
проволока |
|
H / мм2 |
H / мм2 |
- 40°С |
- 60°С |
|
LNS-160 |
|
430 |
510 |
150 |
50 |
| LNS-160 |
400 |
510 |
150 |
50 |
|
| LNS-162 |
470 |
560 |
150 |
100 |
|
| LNS-162 |
450 |
530 |
150 |
100 |
|
| LNS-165 |
530 |
600 |
130 |
50 |
|
|
LNS-165 |
|
480 |
580 |
130 |
50 |
| Характеристики флюса |
| Максимальный ток сварки | 800 Ампер |
| Тип сварочного тока | постоянный прямой и обратной полярности, переменный |
| Плотность | 1.3 кг/дм³ |
| Форма упаковки |
| Наименование | Вес единицы |
| Пластиковый мешок | 25 кг |
| Полипропиленовый мешок | 1000 кг |